J. Korean Ceram. Soc. > Volume 37(8); 2000 > Article
Journal of the Korean Ceramic Society 2000;37(8): 745.
YAG:$Tb^{3+}$ 형광체 분말의 수열합성과 발광 특성
김상문, 지성훈1, 구자인1, 김태옥1
LG전자(주) Display사업본부 Display Device연구소
1부산대학교 공과대학 무기재료공학과
The Luminescence Properties of YAG:$Tb^{3+}$ Phosphor Prepared by Hydrothermal Synthesis
ABSTRACT
YAG:Tb3+ as green phosphor were studied for the development of low voltage FED phosphor prepared by hydrothermal synthesis. We changed the concentration of luminescence center ion Tb3+ in hydrothermal reaction of which conditions were at 8M NH4OH as mineralizer, at 35$0^{circ}C$ for 12hrs. As results, we could finally get the YAG:Tb3+ (Y3-xTbxAl5O12) powder of which particle size was about 0.2~1.0${mu}{textrm}{m}$. The excitation spectra and the green emitted spectra of YAG:Tb3+ phosphor powder were observed. When we doped 0.25 mol Tb to YAG, we could observe the maximum cathodoluminescence from YAG:Tb3+ phosphor and the chromaticity coordinate of the phosphor was shown x=0.35, y=0.56 in CIE1931 diagram.
Key words: Phosphor, YAG:$Tb^{3+}$(${Y_{3-x}}{Tb_x}{Al_5}{O_{12}}$), FED, Hydrothermal synthesis
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community