Tape Casting법에 의한 PMS-PZT계 세라믹스 제조 및 전기적 특성
정현제, 나은상, 최성철
한양대학교 세라믹공학과
The Fabrication and Electrical Properties of PMS-PZT Ceramics using a Tape Casting Method
Hyun-Jae Jung, Eun-Sang Na, Sung-Churl Choi
Department of Ceramic Engineering, Hanyang University
After manufacturing 2mol% CdO substitute $0.05Pb(Mn_{1/3}Sb_{2/3})O_3-0.95Pb(Zr_{0.52}Ti_{0.48})O_3$ piezoelectric ceramics powder as starting material, to manufacture green sheets using Doctor Blade method. The optimum composition of slurry was studied. Moreover, the sintering properties and the dielectric and piezoelectric properties with variation a thickness of the manufactured sheets were investigated. The optimum of slurry was investigated by the rheology with addition of additives, the sintering condition was decided by TGA. And the properties of sheet were investigated through SEM. XRD. The optimum of slurry was the stablest at dispersant 3.0 wt% to solid loading 30vol%. After, at addition of binder/plasticizer(0.75/0.25) 3.0wt%, viscosity was 7.55Pa${cdot}$s. The dielectric and piezoelectric properties of the sheet were increased a little with the increasing of sintering temperature but were not variable with variation of sheet thickness.
Key words: Tape casting, Slurry, PMS-PZT, Green Sheet
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI