졸-겔법을 이용한 $(Pb_{1-x}Sr_x)TiO_3$ 박막의 제조 및 특성에 관한 연구
선계혁, 윤희한, 황규석1, 김병훈
전남대학교 공과대학 무기재료공학과
1전남대학교 공과대학 무기재료공학
Study on the Preparation and Characteristics of $(Pb_{1-x}Sr_x)TiO_3$ Thin Films by the Sol-gel Process
ABSTRACT
To prepare the dielectric thin films of (Pb1-xSrx)TiO3 (x=0.1, 0.2, 0.3, 0.35, 0.5) by the sol-gel process titanium (IV) isopropoxide (Ti[OCH(CH3)2]4) and Pb Sr, acetate were used therefore the thin films were fabricated by dip-coating method. Stability of the sol decreased with addition of Sr content thin films could be fabricated up to 35mol% Over this range precipitation of sol occured thin films couldn't be obtained. Transmittance of thin films at visible range decreased with the increase of heat-treatment temperature but exhibited transmit-tance above 60% in all case. Moreover transmittance of thin films at visible range slightly increased with of addition of Sr,. When thin film containing 30 mol% srontium was heated at 600℃ the best perovskite phase was obtained. The dielectric constant (ε) was 280 and dielectric loss factor (tan δ) was 0.021 and curie tempera-ture (Tc) decreased with the increase of addition of Sr.
Key words: Dielectric $(Pb_{1-x}Sr_x)TiO_3$, thin film, Acetate, Dip-coating, Perovskite, Transmittance, Dielectric constant
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI