Formation Rate of Tetragonal BaTiO3 Powder by Hydrothermal Synthesis and its Dielectric Property
ABSTRACT
Formation rate of tetragonal BaTiO$_3$powder by hydrothermal synthesis and its dielectric property were studied. Submicron tetragonal BaTiO$_3$ powders were prepared hydrothermally, using Ba(OH)$_2$.8$H_2O$, TiO$_2$(anatase) and KOH as starting chemicals. Characterization via X-ray diffractometry, field emission scanning electron microscopy confirmed that increasing calcination temperatures(from 1100 to 130$0^{circ}C$) promotes the formation of tetragonal BaTiO$_3$. Tetragonal BaTiO$_3$ ceramics, obtained by calcining at 1200 for 3 h after hydrothermal synthesis at 200 for 168 h, exhibited submicron size of 0.5 ~ 0.7 ${mu}{textrm}{m}$ and high relative permittivity.
Key words: Tetragonal $BaTiO_3$, Hydrothermal synthesis, Calcination
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community