J. Korean Ceram. Soc. > Volume 29(8); 1992 > Article
Journal of the Korean Ceramic Society 1992;29(8): 660.
송지암-석회계 ALC에 대한 수열반응 특성 - 배합비에 따른 영향
최병현, 김순환, 안용관1, 이종민
요업기술원
1선경건설
Hydrothermal Reaction Characteristics on the ALC of Pitchstone-Lime System
ABSTRACT
Pitchstone reacted with CaO in hot water(9$0^{circ}C$) and increased its sedimentary volume by forming Ca(OH)2 and calcium silicate hydrates. ALC was prepared from gel at 9$0^{circ}C$ and subsequently autoclaved at 18$0^{circ}C$ by using the property of swelling and the physical properties of ALC was investigated with experimental conditions. When the ratio of pitchstone/CaO was 2 (CaO/SiO2 mol ratio=0.81), bulk density, modulus of rupture and thermal conductivity of the ALC were 0.75g/㎤, 73kg/$textrm{cm}^2$ 0.150 kcal/m.hr.$^{circ}C$, respectively. The crystalline phase of it was mainly tobermorite. Therefore ALC was turned out to be much lightweighted and good thermal insulation.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community