Gas Permeation of Y2O3-SiC Composite Membrane
Daheoi Song, Miewon Jung
School of Biological Sciences and Chemistry, Institute of Basic Science, Sungshin Women's University
ABSTRACT
$Y_2O_3$-SiC composite membrane was dip-coated using $Y_2O_3$ sol solution; this membrane was compared with a non- coated one. Each membrane was characterized by XRD, FE-SEM and BET techniques. Hydrogen and CO permeation were tested with self-manufactured Sievert's type equipment. $Y_2O_3$ coating was enhanced for the selectivity of the membrane ($H_2$ versus CO). The hydrogen permeation was measured at 1 bar with increasing temperatures. In case of the coated membrane, hydrogen permeation was found to be $1.24{times}10^{-7}mol/m^2sPa$ with perm-selectivity of 4.26 at 323 K.
Key words: $Y_2O_3$-SiC composite membrane, Dip-coated, Hydrogen and CO permeation
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI