Molten-salt 방법에 의해 합성되는 판상형 알루미나 분말 표면에 돌기형성 거동
이윤주, 김보연, 신동근, 김수룡, 권우택, 김영희
한국세라믹기술원 에너지효율소재팀
Formation of Asperites on the Plate-like Alumina Particles by Molten-salt Method
Yoon Joo Lee, Bo Yeon Kim, Dong-Geun Shin, Soo Ryong Kim, Woo Teck Kwon, Younghee Kim
Energy Efficient Material Team, Korea Institute of Ceramic Engineering and Technology
Alumina nano-asperites were grown on plate-like alumina particles of which the surface had been covered with a capping agent to control the asperite formation sites on the particles. Utilized alumina source for asperite was nano sized ${gamma}$-alumina, which was prepared by calcination of $Al(OH)_3$ at $600^{circ}C$; silica suspension was used as the capping agent. Plate like alumina particles were covered by silica suspension and continuously heat-treated to $900^{circ}C$ with nano sized ${gamma}$-alumina, as the source material, under molten-salt atmosphere. Asperite growing site were controlled by the degree of coating of the capping agent; 10-20 nanosize of ${theta}$-alumina were formed on the particle surface. On the other hand, alumina particles without capping agent were observed to undergo only step-like crystal growth during heat-treatment.
Key words: Asperite, Crystal growth, Alumina, Capping agent, Molten-salt
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community