Mechanical Properties of Porcelain with Thermally and Chemically Induced Residual Stress on Glaze
Dong-Hwan Kim, Jee-Hun Maeng, Yoon Soo Han, Hyung-Tae Kim, Sung-Churl Choi1, Hyeong-Jun Kim
Korea Institute of Ceramics Engineering & Technology
1Devision of Materials Science and Engineering, Hanyang University
ABSTRACT
In this study, we measured the thermally and chemically induced residual stresses on glaze using the photoelastic method. Porcelain with thermally induced residual stress showed compressive stress of 49 MPa for thermal expansion mismatch and a locally fluctuated stress field over the glaze layer due to compensation of compressive stresses around pores. In the case of chemically strengthened porcelain, the compressive stress on the glaze was 151 MPa which was around 3 times higher than the stress on thermally strengthened glaze. The trend of fracture strength of thermally and chemically strengthened porcelains was coincident with that of the residual stress of porcelains.
Key words: Photoelasticity, Glaze, Residual stress, Chemical strengthening
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI