Journal of the Korean Ceramic Society 2011;48(3): 246.
doi: https://doi.org/10.4191/kcers.2011.48.3.246
고체산화물연료전지 연결재용 La0.7Ca0.3Cr0.9Co0.1O3-δ 조성계에 Ca Source 변화에 따른 소결 및 전기적 특성에 관한 연구
박성태, 최병현, 지미정, 안용태, 최헌진1
한국세라믹기술원 전자.광 소재센터
1연세대학교 세라믹공학과
Effects of Ca-Source on the Sintering and Electrical Properties of La0.7Ca0.3Cr0.9Co0.1O3-δ for Solid Oxide Fuel Cell Interconnects
Sung-Tae Park, Byung-Hyun Choi, Mi-Jung Ji, Yong-Tae An, Heon-Jin Choi1
Electronic & Optic Materials Center, KICET
1Department of Ceramic Engineering, Yonsei University
Effects on sintering and electrical properties of $La_{0.7}Ca_{0.3}Cr_{0.9}Co_{0.1}O_{3-{delta}}$ system, a interconnect material for cylindrical and flat tubular solid oxide fuel cells (SOFC), have been investigated by Ca-source when using $CaCO_3$ and $CaF_2$. When using $CaCO_3$ and $CaF_2$ was mixing as Ca-source, single phased perovskite solid solution was observed for each sample. The sintering temperature was decreased by $CaF_2$ contents was increased. When using 0.1 mole $CaF_2$ was densely sintered at $1400^{circ}C$ and relative density was 93.8%. Also, electrical conductivity in oxidation and reducing atmosphere was 47, 4.3 S/cm, respectively, due to $F^-$ ion enhance the electrical conductivity in reducing atmosphere.
Key words: Solid oxide fuel cell (SOFC), Interconnect, Ca-source, $CaF^2$
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI