지르코니아 겔에서 열처리에 따른 광발광의 변화
한규석, 고태경
인하대학교 신소재공학부
Variation of Photoluminescence in Zirconia Gel by Pyrolysis
Kyu-Suk Han, Tae-Gyung Ko
Division of Materials Science and Engineering, Inha University
ABSTRACT
In this study, we prepared zirconia gel by the sol-gel method and investigated its photoluminescence properties by varying pyrolysis temperature. The addition of acetic acid into a Zr-alkoxide solution resulted in forming the bidentate ligands with Zr ions and producing a stable gel. At the pyrolysis temperature of $350^{circ}C$, the zirconia nanocrystals with tetragonal structure gradually appeared in the gel. The PL intensity of the zirconia gel increased with increasing the pyrolysis temperature up to $350^{circ}C$, but decreased above the temperature. Concurrently, its PL peak wavelength continuously shifted from ${sim}440;nm$ to ${sim}550;nm$ with the temperature. The PL characteristics of the zirconia gels were closely associated with decomposition of residual organic groups, the formation of the zirconia nanocrystals, and the tetragonal to monoclinic phase transformation.
Key words: $ZrO_2$, Photoluminescence, Sol-gel, Nanopowder
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI