다공질 지르코니아 세라믹스의 기공율 제어 |
채수호, 엄정혜, 김영욱, 송인혁1, 김해두1, 배지수2, 나상문2, 김승일2 |
서울시립대학교 신소재공학과 1재료연구소(KIMS) 2(주)영진세라믹스 |
Porosity Control of Porous Zirconia Ceramics |
Su-Ho Chae, Jung-Hye Eom, Young-Wook Kim, In-Hyuek Song1, Hai-Doo Kim1, Ji-Soo Bae2, Sang-Moon Na2, Seung-Il Kim2 |
Department of Materials Science and Engineering, the University of Seoul 1Powder Materials Research Division, Korea Institute of Materials Science 2Young-Jin Ceramics Co., Ltd. |
|
|
|
ABSTRACT |
A simple pressing process using zirconia and microbead for fabricating porous zirconia ceramics is demonstrated. Effects of microbead content and sintering temperature on microstructure, porosity, compressive and flexural strengths were investigated in the processing of porous zirconia ceramics using microbead as a pore former. By controlling the microbead content and the sintering temperature, it was possible to produce porous zirconia ceramics with porosities ranging from 43% to 70%. Typical compressive and flexural strength values at ${sim}50%$ porosity were ${sim}150;MPa$ and ${sim}35;MPa$, respectively. |
Key words:
Porous ceramics, Zirconia, Processing, Porosity |
|