Brookite TiO2 코팅용 졸의 제조 및 광촉매 효과
김선재, 이남희, 이강, 최창주1
세종대학교 나노공학과/나노신소재공학연구소
1조선대학교 전기공학과
Preparation and Photocatalytic Effect of Brookite Phase TiO2 Colloidal Sol for Thin Film Coating
Sun-Jae Kim, Nam-Hee Lee, Kang Lee, Chang-Joo Choi1
Department of Nano Science and Technology/SAINT, Sejong University
1Department of Electrical Engineering Chosun University
Transparent TiO$_{2}$ sols were prepared by hydrothermal synthesis to heat Ti precursor solutions, from Ti hydroxides obtained with neutralizing aqueous TiOCl$_{2}$ solutions having various concentrations of NaCI by aqueous NaOH solution, in the autoclave at 120$^{circ}C$ The photocatalytic abilities of glass beads coated with the sol for gaseous benzene were evaluated. As a result, it was found that due to the increase of brookite phase in TiO$_{2}$ by controlling the concentration of Na ion the optical absorption of TiO$_{2}$ increases toward long wavelength but that in the area of short wavelength becomes relatively low and consequently the photocatalytic performance of TiO$_{2}$ thin film for benzene gas rather decreases, compared to that of composite film of anatase and brookite phases. These results suggest that in order for coated TiO$_{2}$ thin film to have high dissociation performance for benzene gas it is effective to form anatase and brookite phases compositely in TiO$_{2}$.
Key words: TiO2 Brookite, Photocatalyst, Colloidal sol, Thin film
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community