J. Korean Ceram. Soc. > Volume 40(12); 2003 > Article
Journal of the Korean Ceramic Society 2003;40(12): 1213.
doi: https://doi.org/10.4191/kcers.2003.40.12.1213
수열반응을 이용한 미생물 담체용 다공성 세라믹스의 제조
양성구, 정승화1, 강종봉2
경남대학교 공동기기센터(대학원 재료공학과)
1경남대학교 재료공학과
2경남대학교 신소재공학부
Fabrication of Porous Ceramics for Microorganism Carrier by Hydrothermal Reaction
ABSTRACT
Porous ceramics for microoganism carriers were prepared with amorphous alumina and pore formers by hydrothermal reaction, burn-out and wash-out method. Activated carbon with average size of 67,222, and 405 $mutextrm{m}$, organic polymer and inorganic salt were used as pore formers. Specimens were hydrothermally treated at 200$^{circ}C$ for 24 h, heat-treated at 650$^{circ}C$ for 5 h, and washed out at 80$^{circ}C$ for 48 h. The formation of crystalline phase, porosity, pore size distribution and compressive strength were measured. The specimen with activated carbon was transformed to boehmite phase, but organic polymer and inorganic salt inhibited the aquohydroxoy complex gel and crystalline formation. The porous ceramics for microoganism carriers using activated carbon as a pore formers was successfully prepared, which is composed of ${gamma}$-alumina phase with porosity of above 70 vol% and the compressive strength of 40 kgf/$textrm{cm}^2$.
Key words: Microorganism carrier, Amorphous alumine, Hydrothermal reaction, Pore former
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI