| Fabrication and Properties of Reaction Bonded SiC Hot Gas Filter Using Si Melt Infiltration Method |
|
|
|
|
|
|
|
| ABSTRACT |
|
Novel fabrication technique was developed for high strength Reaction-Bonded SiC (RBSC) hot gas filter for use in IGCC (Integrated Gasification Combined Cycle) system. The room and high temperature fracture strengths for Si-melt infiltrated reaction-bonded SiC were 50-123, and 60-66 MPa, respectively. The average pore size was 60-70 $mutextrm{m}$ and the porosity was about 34 vol％. RBSC infiltrated with molten silicon showed improved fracture strength at high temperature, as compared to that of clay-bonded SiC, due to SiC/Si phase present within SiC phase. The thickness for SiC/Si phase was increased with increasing powder particle size of SiC from 10 to 34 $mutextrm{m}$. Pressure drop with dust particles showed similar response as compared to that for Schumacher type 20 filter. The filter fabricated in the present study showed good performance in that the filtered powder size was reduced drastically to below 1 $mutextrm{m}$ within 4 min. |
| Key words:
RBSC, Infiltration, Si, SiC |
|
|
|
PDF Links
Full text via DOI
Download Citation 