Journal of the Korean Ceramic Society 2001;38(11): 1042.
BZN-SZN계 세라믹스의 마이크로파 유전 특성에 미치는 $ZrO_2$의 영향
윤석규, 박우정, 양우석, 윤대호
성균관대학교 신소재공학과
Effect of $ZrO_2$Addition on the Microwave Dielectric Properties of BZN-SZN System Ceramics
Microwave dielectric properties of Ba(Zn$_{1}$3/Nb$_{2}$3/) $O_3$-Sr(Zn$_{1}$3/Nb$_{2}$3/) $O_3$(BZN-SZN) system were investigated as a function of sintering temperature and Zr $O_2$content. Density was increased and the temperature coefficient of resonant frequency (TCF, $tau$$_{f}$) decreased with increasing sintering temperature. However dielectric constant (K) and Q$times$f value did not change markedly with the sintering temperature. For the samples sintered at the same temperature, density, dielectric constant, and Q$times$f value were increased and TCF was decreased with increasing Zr $O_2$concentration. Especially, the dielectric constant of the sample increased with x and exhibited the maximum value ($varepsilon$$_{r}$=41) when x=0.6 at 1575$^{circ}C$ sintered. TCF decreased with x and exhibited the minimum value ($tau$$_{f}$=+0.8ppm/$^{circ}C$) when x=1.0..0.
Key words: BZN-SZN, $ZrO_2$, Microwave, Dielectric properties, TCF
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community