소결 분위기와 조성이 $TiB_2$-AlN-BN 복합체의 반응 가압 소결에 미치는 영향
이기민, 김형종, 최헌진, 이준근
한국과학기술연구원 복합기능세라믹스센터
Effect of Atmosphere and Composition on the Fabrication of $TiB_2$-AlN-BN Composites by Reactive Hot Pressing
Effects of the chemical composition and sintering atmosphere on the formation of reaction phases and physical properties of reactive hot-pressed TiB2-AlN-BN composites were investigated. At N2 atmosphere, TiN was formed by the reaction between Ti and N2, which inhibited the densification and results in inferior mechanical-and electrical properties of the composites. However, at Ar atmosphere, enhanced densification and physical properties of composites were obtained due to that the TiN formation reaction was excluded. Densification of the composites was also hindered by BN, therefore, inferior mechanical-and electrical properties of composites were obtained with amount of BN in the starting materials. At Ar atmosphere, TiB2-AlN-BN composites having 318 MPa of flexural strength, 3.5 MPa.m1/2 of fracture toughness and 276$mu$Ω.cm of electrical resistivity were fabricated from mole ratio 1:2:1.6 of Ti-Al-BN mixtures.
Key words: Tutanium diboride, Composites, Reactive hot pressing, Properties
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI