질화 규소 접합체의 미세구조와 파괴 강도에 관한 연구
차재철, 강신후, 박상환1
서울대학교 재료공학부
1한국과학기술원
Microstructure and Fracture Strength of Si3N4 Joint System
ABSTRACT
Si3N4 -Si3N4 joints were made using Ag-Cu-Ti and Ag-Cu-In-Ti via brazing method and the change in joint strength was investigated after heat treatment at 400$^{circ}C$ or 650$^{circ}C$ for up to 2000h. The initial strength of as-brazed joints with Ag-Cu-In-Ti was lower but the reduction of the strength was less dramatic than that with Ag-Cu-Ti. The joints made of a new brazing alloy Au-Ni-Cr-Mo-Fe which is developed for high temperature applications were heat-treated at 650$^{circ}C$ for 1000h. As the heat treatment time increased the bond strength increased. The results of the joining system with Mo or Cu interlayer showed that the strength of the joint with Mo interlayer was higher but the system incurred problems in joint production Also it was found from oxidation experiment that Ti and In affected the oxidation resistance of brazing alloy
Key words: Brazing, Si3N4 joint, Ag-Cu-Ti, Ag-Cu-In-Ti, Reliability
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community