CuO 첨가에 따른 $Y_3$Fe$_5$O$_{12}$ 소결체의 미세구조 변화
이재동, 김광석, 김성재1, 김태옥
부산대학교 공과대학 무기재료공학과
1국방과학연구소
Dependence of Microstructure of Sintered $Y_3$Fe$_5$O$_{12}$ in Addition of CuO
ABSTRACT
As results of the study on the sinterbility of YIG at the low temperature using CuO as additive CuO com-pound which contain {{{{ { {Fe }_{2 }O }_{3 } }} was shown liquid in sintering process. YIG crystal dissolved into CuO compound liquid phase and then Y element which is considered no solubility in solid CuO compound moved to the grain during cooling. The abnormal grain growth up to 150${mu}{textrm}{m}$ at CuO 8.6mole% was shown due to shape accomdation reaction and local liquid distribution. The apparent density of YIG shows minimum at CuO 8.6 mole% due to abnormal grain growth and the saturation magnetization decrease dramatically at 32.5mole% due to orthoferrite formation.
Key words: Granet, YIG, Magnetism, Orthoferrite
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI