액상 Ni/Si/Co 침투에 의한 반응결합 TiC 복합체의 치밀화 |
한인섭, 우상국, 배강, 홍기석1, 서두원, 정윤중 |
한국에너지기술연구소 에너지재료연구팀 1한국에너지기술연구소 에너지재료연구 |
Densification of Reaction Bonded TiC Composite by Infiltration of Liquid Phase Ni/Si/Co |
|
|
|
|
|
ABSTRACT |
The reaction-bonded TiC-Ni/Si/Co composites were prepared by the melt infiltration of Co, Si, and Ni me-tal into the TiC preforms. The miocrostructure reaction composition and mechanical properties were in-vestigated. In the case of the melt infiltrated with Co and Ni TiC grain shape was changed from angular to spherical shape with the average grain size of ∼5$mutextrm{m}$. In the case of the melt infiltrated with Co/Si or Ni/Si, Si was reacted with TiC particles and formed SiC particles. The bending strength of both specimens which have atomic ratio of 3 were 710 MPa and 515 MPa respectively. In the case of the melt infiltrated with Ni/Si/Co,. nonstoichiometric TiC was formed and its bending strength decreased to 420 MPa. |
Key words:
Melt infiltration, TiC compostie, Reaction-bonded sintering, Co/Si/Ni melt |
|