SHS법에 의한 $Ti_xZr_{1-x}C$ 고용체의 합성 및 특성 연구
이형복, 오유근1, 이성민
명지대학교 무기재료 공학과
1요업기술원
A Study on Synthesis and Characterization of $Ti_xZr_{1-x}C$ Solid-Solution by Self-propagation High Temperature Synthesis Method
ABSTRACT
TixZr1-xC(0$0^{circ}C$, 5.1 mm/sec respectively. The relative density, three point flexural strength, and the hardness of composites, which was sintered at 190$0^{circ}C$ for 60 min by using hot-pressing under a pressure of 30 MPa, were 99%, 525 MPa and 24 GPa respectively.
Key words: TiZrC solid solution, SHS method, Composite, Temperature profile
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI