$(Pb, Nd)(Ti, Mn)O_3$ 세라믹의 유전 및 압전특성
임주수, 신혁재, 오태희1, 김종희1, 송병무1, 이재신
울산대학교 재료공학과 금속공학과
1쌍용양회공업(주) 주앙연구소
Dielectric and Piezoelectric Properties of $(Pb, Nd)(Ti, Mn)O_3$ Ceramics
Dielectric and piezoelectric properties of (Pb1-1.5xLnx)(Ti0.98Mn0.02)O3 ceramics with x=0~0.2 have been investigated. Pb(Ti0.98Mn0.02)O3 showed poor sinterability and cracking on cooling, but the substitution of Nd3+ ions into Pb2+ sites resulted in dense microstructures without cracking through reducing crystallographic anisotropy. The Nd3+ substitution, however, deteriorated the temperature stability of the piezoelectric properties because of lowering the Curie point. Electromechanical anisotropy(Kt/Kp) indicated a maximum value of 10 when x=0.1. This result might be attributed to the counteracting effects that with increasing x, the lattice anisotropy decreases while the poling becomes easier due to the increase in O2- vacancy concentration. Thickness-shear mode resonators with (Pb0.85Nd0.1)(Ti0.98Mn0.02)O3 composition showed good resonant characteristics around 4.5 MHz.
Key words: Lead titanate, Piezoelectric ceramics, Neodymium, Ceramic resonator
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community