Journal of the Korean Ceramic Society 1995;32(7): 853. |
졸-겔법에 의한 지르콘$(ZrSiO_4)$ 분말 합성 -재분쇄(Milling)에 대한 효과- |
신용철, 신대용, 한상목, 남인탁 |
강원대학교 재료공학과 |
Synthesis of $(ZrSiO_4)$ Powders by the Sol-Gel Process -Effect of the Milling- |
|
|
|
|
|
ABSTRACT |
ZrSiO4 powders were prepared from partially hydrolyzed solution of Si(OC2H5)4 and ZrOCl2.8H2O solution by the sol-gel method and formation rate of ZrSiO4 on the reaction parameter was investigated. In order to prepare homogeneous ZrSiO4 precursor gels, the H2O/Si(OC2H5)4 molar ratio of about 2, the pH of the ZrOCl2.8H2O solution fo about 4 and stirring time of the mixed solutions of about 2 hrs were appropriate. Formation of temperature of ZrSiO4 reduced about 15$0^{circ}C$ by milling and formation of ZrSiO4 at 1300~135$0^{circ}C$ showed an accelerative increase through the hedvall effect by silica. |
Key words:
Zircon, $Si(OC_2H_5)$, $ZrOCl_2 |
|
|
|