$UO_2$ 소결체의 산화/환원에 의해 제조된 분말 특성
김봉구, 송근우, 이정원, 배기광, 양명승, 박현수
한국원자력연구소
Characteristics of Powder Prepared from Unirradiated $UO_2$ Pellets by Oxidation and Reduction Method
ABSTRACT
Unirradiated UO2 pellets were pulverized by oxidation in air at 40$0^{circ}C$, and the oxidized powders were reduced in H2 and CO atmospheres at $600^{circ}C$. During the oxidation of UO2 at 40$0^{circ}C$, intergranular cracks which caused the spallation were mainly developed by the volume contraction due to the formation of intermediate phase (U4O9 or U3O7). As oxidation proceeded, U3O8 finally formed. As the oxidation/reduction cycles were repeated, the powder surface became coarser, specific surface area was increased and average particle size was decreased. The sintered densities of the powder were increased by the oxidation/reduction cycle due to the characteristic changes of the powder.
Key words: Uranium oxide, Oxidation, Reduction, Powder characteristics
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI