Hot Pressing에 의한 $Si_3N_4-SiC$ 나노복합체의 제조
김성현, 김인술1, 박홍채, 오기동
부산대학교 무기재료공학과
1포항제철 기술연구소
Fabrication of $Si_3N_4-SiC$ Nanocomposites by Hot Pressing
ABSTRACT
SiC ultrafine particles of 1, 10, 20 and 30 vol% were dispersed in $alpha$-Si3N4 matrix and hot-pressed under the condition of 30 MPa at 1800 and 190$0^{circ}C$ respectively. Physical, mechanical properties and microstructures of sintered Si3N4-SiC nanocomposites were investigated. Flexural strength and density of Si3N4-10 vol% SiC nanocomposites hot-pressed at 190$0^{circ}C$ represented the 1002 MPa and 97.9%T.D respectively, and it was confirmed as a remarkable improvement of 67% compared to Si3N4 monolith. Fracture toughness was shown as 7.2 MPa.m1/2 when the same composition was hot pressed at 180$0^{circ}C$. This effect was supposed to be due to the improvement of microstructure by the adequate suppression of the excessive growth of Si3N4 grain with SiC nano-particles.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community