J. Korean Ceram. Soc. > Volume 31(9); 1994 > Article
Journal of the Korean Ceramic Society 1994;31(9): 969.
$3Y-ZrO_2$$8Y-ZrO_2$ 분말의 혼합비율에 따른 테이프 캐스트된 지르코니아 박판의 전기적 성질의 변화
김선재, 강대갑, 김경호, 정충환, 박지연
한국원자력연구소 정밀요업재료 개발팀
Electrical Properties of Tape-Cast Zirconia Thin Plates with the Mixing Ratios of $3Y-ZrO_2$ and $8Y-ZrO_2$ Powders
ABSTRACT
After adding 8Y-ZrO2 powders to 3Y-ZrO2 powders at ratios of 0, 33, 50, 67, and 100% by weight, the mixed yttria-stabilized zirconia specimens were fabricated into thin plate using tape~casting method and then sintered at 150$0^{circ}C$ for 4h in air. The crystalline structure, microstructure and electrical properties of the sintered zirconia thin plates were investigated by using X-ray diffractometer, scanning electron microscope and impedance analyser, respectively. At the temperatures higher than 75$0^{circ}C$, the sintered thin plate with 33% 8Y-ZrO2 content shows higher mechanical properties and lower electrical resistivity than 8Y-ZrO2 thin plate which is generally used as an electrolyte for solid oxide fuel cells. This is due to the fact that the zirconia thin plates with low 8Y-ZrO2 content maintain the slope of low temperature region up to high temperatures, whereas at temperatures higher than 50$0^{circ}C$ the slope decrease in the zirconia thin plates with high 8Y-ZrO2 content.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community