섬유보강 시멘트 모르타르의 기계적 특성
정민철, 남기웅, 정윤중
명지대하교 공과대학 무기재료공학과
Mechanical Properties of Cement Mortar with Fibers
A fiber reinforced grouts were made using ordinary cement mortar and high effective water reducing agent (naphthalene sulfonate) were made by addition polypropylene fiber and carbon fiber. The physical properties of the grouts were investigated through the observation of the microstructure and the application of fracture mechanics. When the polypropylene fiber and carbon fiber were added respectively with 0.03 wt% to the grouts the compressive strength, flexural strength and Young's modulus were about 60∼63 MPa, 12.2∼12.4 MPa, 4.2∼4.8 GPa and 63∼68 MPa, 12.2∼12.6 MPa, 4.8∼5.1 GPa, and critical stress intensity were about 0.77∼0.82 MNm-1.5, and 0.80∼0.87 MNm-1.5 respectively, It can be considered that the strength improvement of fiber reinforced grouts (FRG) may be due to the removal of macropores and the increase of various fracture toughness, polymer fibril bridging and fiber bridging.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI