J. Korean Ceram. Soc. > Volume 31(4); 1994 > Article
Journal of the Korean Ceramic Society 1994;31(4): 427.
저온소결 세라믹기판용 Cordierite계 결정화유리의 합성 및 특성조사에 관한 연구;(IV) Sol-Gel법으로 코팅한 Cu분말을 이용한 Metallizing
김병호, 문성훈, 이근헌, 임대순
고려대학교 재료공학과
Synthesis and Characterization of Cordierite Glass-Ceramics for Low Firing Temperature Substrate; (IV) Metallizing by Using Cu Powder Coated by Sol-Gel Method
Cu-metallized low firing temperature substrates were synthesized by cofiring green sheet of cordierite-based glass with Cu. By Sol-Gel method, Cu powder was coated with borosilicate gel which should act as a glass frit in Cu paste during cofiring. Theoretical weight ratios of Glass/Cu were controlled to be 2.5, 5, 10 and 15% by varying alkoxide concentrations. Average particle size of coated Cu was 0.629~0.674 ${mu}{textrm}{m}$ in comparison to that of as-received Cu(0.596 ${mu}{textrm}{m}$), which increased with alkoxide concentration but did not increase above certain concentration. The weight ratios of coated layer were 2.11~5.37%. The properties of Cu-metallized low firing temperature substrate, cofired at 90$0^{circ}C$ for 1h under H2/N2 atmosphere, were as follows; sheet resistance was 13~43 m{{{{ OMEGA }}/$square$, adhesion strength was 1.0~2.1 kgf/$textrm{mm}^2$. From the observations of SEM photographs, the gel coated on Cu performed excellently as a glass frit.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI