J. Korean Ceram. Soc. > Volume 30(2); 1993 > Article
Journal of the Korean Ceramic Society 1993;30(2): 164.
표면 연마가 3Y-TZP의 저온열화에 미치는 영향
김대준, 이홍림1, 정형진
한국과학기술연구원 재료연구단
1연세대학교 세라믹공학과
Effect of Surface Grinding on Low Temperature Degradation of 3Y-TZP
ABSTRACT
Grinding of 3mol% Y-TZP enhanced the texturing of t-ZrO2, which is represented by the increased I(002)t/I(200)t peak intensity ratio, and an asymetric broadening of (111)t peak. The degree of texturing and asymetric broadening depended on a seversity of grinding. The asymetric (111)t peak broadening was resulted by the formation of r-ZrO2. When aged at 25$0^{circ}C$ for 120h, r-ZrO2 transformed to t-ZrO2 due to the relief of stressed surface area and the amount of tlongrightarrowm transformation inversely varied with the I(002)t/I(200)t. The inverse dependence was interpreted by that the degree of texturing determines the magnitude of residual surface stress and the lattice relaxation of t-ZrO2, which causes the low temperature degradation, is retarded as the residual stress becomes greater.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI