J. Korean Ceram. Soc. > Volume 27(4); 1990 > Article
Journal of the Korean Ceramic Society 1990;27(4): 521.
$Li_2O$.$2SiO_2$. 유리의 결정화와 투광성에 관한 연구
최병현, 안재환, 지응업1
아주대학교
1동양공업전문대학
Crystallization and Transparency of $Li_2O$.$2SiO_2$ Glass-Ceramics
ABSTRACT
Li2O.2SiO2 glass-ceramics were made from the melt by the nucleation and growth treatment. The optimum nucleation temperature and time were determined from DTA curves of as-quenched and thermally treated glasses, and found to be 44$0^{circ}C$ and 3hrs. The optical microscopic technique was also used to support this result. The volume fractions of crystals present in the partially crystallized specimens were measured using the optical microscopy and the amorphous X-ray scattering methods. The degree of crystallization increased with increasing the crystallization temperature and time. The crystalline phase identified by X-ray diffraction was lithium disilicate. As the crystallinity increased up to 95%, the transmittance of glass-ceramics was decreased linearly. It was also found that for the same heat treatment condition (575$^{circ}C$, 30min), a thicker specimen showed higher transmittance, presumably due to less crystallinity.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI