J. Korean Ceram. Soc. > Volume 25(2); 1988 > Article
Journal of the Korean Ceramic Society 1988;25(2): 184.
염화지르코늄(IV)으로부터 질화지르코늄 미분체의 합성에 관한 연구
김영우, 장윤식, 박홍채, 오기동
부산대학교 무기재료공학과
A Study on the Synthesis of Fine Zirconium Nitride Powder from Zirconium Chloride(IV)
ABSTRACT
ZrN powder was prepared from the powder mixture of ZrCl4 and Al by the halogenide process in nitrogen gas flow (100-150ml/min) at the temperatures from 200$^{circ}$to 1050$^{circ}C$. ZrN powder was formed about 600$^{circ}C$ and in the slow nitriding reaction, however, an intermediate product of Al3Zr was formed. The fine powder (0.1-10$mutextrm{m}$) of single phase ZrN was obtained at 1050$^{circ}C$ after 1 hour. The lattice parameter and crystallite size of ZrN were 4.5787A and 360A, respectively. According to SEM observation, the particles were apt to agglomerates. The apparent activation energy for the formation of ZrN was approximately 13.2kcal/mole(750$^{circ}$-1000$^{circ}C$).
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI