Barium Titanate를 고상반응으로 합성할때 일어나는 이상팽창에 관한 연구
이은상, 임대영
한양대학교 무기재료공학과
A Study of Abnormal Expansion to be Synthesized Barium Titanate in Solid-solid Reaction
ABSTRACT
When the barium titanate is Synthesized in Solid-solid reaction the abnormal expansion occurs at about 110$0^{circ}C$. The mixture was made of corresponding to the theoretical composition of barium titanate. The mixture was fired at various temperature from 90$0^{circ}C$ to 130$0^{circ}C$, After that the specimen was tested closely with XDR dilatometer and SEM. The results indicate that 1, The activation energy of barium titanate formation was 42 Kcal/mole. 2, Thermal expansion up to to 90$0^{circ}C$ was mainly caused by $CO_2$ whereas it was mainly caused by the formation of the secondary phase above 100$0^{circ}C$. 3. Thermal expansion was not influenced by the forming pressure up to 1000kg/$cm^2$ but it was largely influenced bythe forming pressure above 200kg/$cm^2$
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI