Journal of the Korean Ceramic Society 1985;22(2): 3.
$Li_2O$.$Al_2O_3$.$SiO_2$ 계 유리에서 RO치환 및 $R_2O_3$ 첨가에 따른 결정화 특성
이종민, 김무경, 최병현1, 양중식2
국립공업시험원 요업과
1도자기시험소 제품과
2경희대학교 화학과
The Crystallization Characteristics Change in $Li_2O$.$Al_2O_3$.$SiO_2$ System Glass-Ceramics when Varying of RO Ratio and Increasing $R_2O_3$
In the study the characteristics change of crystallized $Li_2O$.$Al_2O_3$.$SiO_2$ glass-ceramics when varying RO ratio and increasing Al2O3 were investigated to produce a glass-ceramics with high mechanical strength and low thermal expansion. Parent glass was obtained by melting at 1,350~1,40$0^{circ}C$ for 3 hours and annealing at 45$0^{circ}C$ and the various physical characteristics were measured. Results were as follows; 1. When ZnO was replaced by MgO thermal expansion coefficient was lowered when increasing ZnO content. 2. Major crystal phase was $beta$-spodumene the crystal growth mophology was the three dimensional sphere and the activation energy for crystallization was 54.6 Kcal/mol. 3. Parent glass heat-treated at 95$0^{circ}C$ for 10 hours had ; a) thermal expansion coeff. of $23.2{times}10^{-7}$/$^{circ}C$ b)whiteness of 76 c) microhardness of 1,089kg/$mm^2$
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI