공심물의 숙성이 Ba-Ferrite의 합성과정에 미치는 영향
김태옥, 김은동
부산대학교 무기재료공학과
Effect of Aging Coprecipitate on the Synthesis Process of Ba-Ferrite
The effect of aging coprecipitate obtained by the reaction of mixed solution 1.1 mol FeCl-0.1 mol $BaCl_2$ and 4.0 mol. NaOH-1.0 mol $K _2 CO_3$ on the synthesis process of Baferrite $(BaFe_{12}O_{19})$ was investigated by means of DTA, TGA, XRD and electron microscope. The no-aged coprecipitate seems to be the aggregate of amorphosus $Fe_3$ .$nH_2O$ and (1-X) $BaCO_3$.$xBa(OH)_2$, but the 30 days-aged to be composed of crystalline $Fe_2O_3H_2O$ and $BaCO_3$. The decomposition temperature of $BaCO_3$ in the coprecipitate increases from 400-$700^{circ}C$ to 700-90$0^{circ}C$ with increment of aging-time. In the no-aged coprecipitate Ba-ferrite is synthesized through the surface reaction of amorphous Fe_2O_3$ and skeleton crystal BaO at 800-90$0^{circ}C$ with more compact crystalization. During calcination of the 30 days-aged coprecibitate the intermediate phase BaFe_2O_4$ is formed at 600-$700^{circ}C$ and completely transformed to Ba-ferrite at 800-90$0^{circ}C$
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI