Journal of the Korean Ceramic Society 1983;20(4): 324.
고주파용 절록재료로서의 Forsterite 자기에 관한 연구(III) (Forsterite 자기의 미구조와 열팽창, 비저항과의 관계)
이은상, 황성연
한양대학교 무기재료공학과
A Study on the Forsterite Porecelain as a High Frequency Insulator(III) (Microstrucrue, Thermal Expansion and Resistivity of the Forsterite Porcelain)
ABSTRACT
In this studies resistivity thermal expansion and microstructure of the Forsterite Porcelain as a high frequency insulator were investigated. The body containing Zn-glass shows higher resistivity than any other body. The bodies containing K, Ba, Cd-glass respectively consist of fine crystals of mosaic type. The bodies containing Bi, Zn, Zr-glass repectively included more large crystals because of the grain growth and coherence of fine particles In the 4 series Forsterite containing excess MgO 0-6% the thermal coefficients of the bodies increased with the increasing of excess MgO and the bodies have conspicuously high thermal expansion coefficients when 15% excess $BaCO_3$ was added to. The resistivities of additive bodies of $BaCO_3$ 0, 5, 10% in Forsterite containg excess MgO 2% are higher than any other that of composition. Bacause the growing of Forsterite crystals was restrained with the increasing of excess MgO $BaCO_3$ their grain size became fine and their grain boundaries were decomposed and also the glass phase having high refractive inder was increased. The higher the firing temperature increased the more the process of crystal growing was progressed.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community