J. Korean Ceram. Soc. > Volume 20(3); 1983 > Article
 Journal of the Korean Ceramic Society 1983;20(3): 243.
 $MgO-SiO_2$ 계 자기에 관한 연구(II) 이응상, 이종근, 최성철1, 안기성 한양대학교1한양대학 A Study on the Porcelain Body of $MgO-SiO_2$ System(II) ABSTRACT This study has examined on the effect for the fitting in porcelain body of MgO-SiO system. The mixture was made of correponding in the theoretical composition of enstatite with Kyul Sung Talc and sea water magnesia cake. Hyup Jin Kaolin as clay minerals to give the mixture plasticity was added 10% by weight of the mixture. Feldspar was added inv various kinds of 1%-20% by weight of the above mixture. After the physical properties and microstructures were carefully examined the following results were obtained. 1. The addition amount of feldspar should generally be from 5% to 10% by weight of the mixture to be good for the properties of the strength and the range of the firing temperature. 2. The 5% addition amount of feldspar was good for the apparent bulk density. 3. 5% and 10% additions showed up stably excellant with respect to the various properties Therefore when we considered the apparent bulk density and the thermal shock resistance 5% addition amount of feldspar showed the most excellant properties between $1350^{circ}C$ and $1400^{circ}C$
TOOLS
Full text via DOI
 Related articles A Study on the Saturation of Grain Size in Pb(Zr, Ti)$O_3$ Thin Films  2000 ;37(6) A Study on the Crystal Structure of $SrNd_2Ti_4O_12$  1999 ;36(11) A Study on Synthesis an Mechanical Properties of $TiB_2-B_4C$ Composite by SHS Method  1999 ;36(9) A Study on Synthesis and Characterization of TiZrB$_2$ Composite by SHS Microwave  1999 ;36(1) A Study on the Growth of ZnGa$_2$O$_4$ Thin Film Phosphors  1998 ;35(2)