J. Korean Ceram. Soc. > Volume 20(3); 1983 > Article
 Journal of the Korean Ceramic Society 1983;20(3): 217.
 $CaO-ZrO_2$계 소결체의 상변화와 미구조에 관한 연구 박금철, 최영섭 한양대학교 무기재료공학과 A Study on Microstructure and Phase Transformation of Sintered Body in $CaO-ZrO_2$ System ABSTRACT Adquate amount of calcia was added to the regent-grade Zirconia body. Here the amount and the form of calcia were 7-21 mol% and regent-grade calcium cabonate respectively. The specimens were fired at 175$0^{circ}C$ for 0, 3, 5 and 7 hours respectively. The phase Strength X-ray diffraction analysis and Scaning electron microscopy. The results were as follows (1) As the additive amount of calcia was increased the firing linear shrinkage apparent density compressive strength and modulus of rupture decreased but the apparent porosity increased. (2) The specimens soaked and containing calcia displayed the grain growth. (3) Monoclinic and cubic zirconia were seen in the sepcimens containing 7 mol% calcia. When without soaking the specimens containing 7-10 mol% calcia had the volume change by monoclinic$rightleftharpoons$tetragonal transformation. (4) The lattice parameter increased according as the calcia additive was increased. The specimens containing above 19mol% calcia had the costant lattice parameter. The value of that was from 5.1264 to 5.1396 $AA$ in the case of 7 hours soaking.
TOOLS
Full text via DOI
 Related articles A Study on the Saturation of Grain Size in Pb(Zr, Ti)$O_3$ Thin Films  2000 ;37(6) A Study on the Crystal Structure of $SrNd_2Ti_4O_12$  1999 ;36(11) Microstructures and Mechanical Properties of SiC Containing $SiC_{platelet}$ Seeds of Various Size  1999 ;36(10) Microstructure and Fracture Strength of Si3N4 Joint System  1999 ;36(8) Processing and Characterization of a Direct Bonded SOI using SiO$_2$ Thin Film  1999 ;36(8)