J. Korean Ceram. Soc. > Volume 15(1); 1978 > Article
Journal of the Korean Ceramic Society 1978;15(1): 9.
광화제로서 $Fe_2O_3$, $MnO_2$, $CaF_2$$TiO_2$의 혼합물이 Mullite화에 미치는 영향
백용혁, 최상흘1, 정창주, 박현수
전남대학교 요업공학과
1한양대학교 요업공학과
Influence of Mixtures Composed of $Fe_2O_3$, $MnO_2$, $CaF_2$ and $TiO_2$ as Mineralizers on Mullitization
ABSTRACT
The possiblity of mullitization from the domestic alunite by adding of $Fe_2O_3-MnO_2$, $Fe_2O_3-MnO_2-TiO_2$, $Fe_2O_3-MnO_2-CaF_2$, and $Fe_2O_3-MnO_2-CaF_2-TiO_2$ mixtures as mineralizers was studied at the temperature range between $1, 250^{circ}C$~$1, 430^{circ}C$. The modifying method of domestic alunite was performed by calcination, wet ballmilling, and washing with water. The following results were obtained; 1) When added of 3.0% $Fe_2O_3$ plus 1.0-1.5% $MnO_2$ to modified alunite, the appropriate temperature range of mullite-forming was $1, 350^{circ}C$-$1, 400^{circ}C$. 2) When added of $TiO_2$ as mineralizer, the mullite-forming temperature was higher than not added. 3) When added of $CaF_2$ as mineralizer, the synthesized mullite was resolve at the temperature above $1, 350^{circ}C$.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      developed in m2community