Kim, Han, Park, Park, Na, and Choi: New Glaze Composition for Chemical Strengthening of Bone China

Abstract

In order to improve the hardness of commercial bone china, we suggested a chemical strengthening process and new glaze for its process. New glaze contained about two times more Na2O and Al2O3 and had a higher transition temperature than that of commercial frit. Chemical strengthening enhanced the hardness of the new glaze-coated bone china by over 30% compared to that of commercial product. The change of glaze composition influenced potassium ion diffusion distance and depth of strengthened layer during chemical treatment. After chemical strengthening of new glaze-coated bone china, the residual compressive stress inside the glaze was measured and found to be greater than 160 MPa.

1. Introduction

Since the invention of bone china by Thomas Frye in the UK in 1749, bone china has become a high quality ceramic ware.1) Bone china production in Korea started in the 1970s, and the domestic quality level has now come to be on par with products manufactured in advanced nations. The material properties of bone china have continued to be improved since the 2000s through various efforts including the enhancement of the ingredient materials and glaze.2-8)
The Frit glaze used in bone china widely uses ABS (Advanced Borosilicates) without lead, including B2O3-SiO2, Bismuth-Silicate, and Zinc-Strontium.9-11) Especially, the ABS glaze most used in Korea has been reported to have a low refractive index and less gloss compared to lead-based or bismuth glazes;12) however, these are difficult to distinguish with the naked eye.
With regard to chemical strengthening techniques, application research has been carried out with the aim of improving the surface hardness of dental crown products.13,14) Recently, there have been efforts to enhance the surface hardness of bone china due to problems of hygiene, and research by Kim et al. reported the strengthening of glaze by varying the bone china curing conditions and applying chemical strengthening to regular ceramics.15-17)
In this study, as a follow up to a previous study,17) new glaze compositions advantageous for chemical strengthening were proposed. Based on the degree of the improvement and the glass reinforcement mechanism, the presented glazes were analyzed to determine their improvement of the hardness through chemical strengthening.

2. Experimental Procedure

The glaze used for comparison in this study was the commercially available bone china glaze manufactured by H company. Although there was a restriction that the entire composition of the commercial glaze cannot be revealed, the contents of the core materials, Al2O3 and Na2O, were 7.4 and 6.3 wt%, respectively (Table 1). The composition of the Frit presented in this study was varied by increasing the SiO2 and Al2O3 contents with the prediction that the resulting product would be stronger in comparison to a glass structure. The Na2O content was more than double that of the reference commercial Frit. Compared to other alkaline earth oxides, CaO addition was disadvantageous for chemical strengthening, so the CaO content was decreased to less than about 1/3 in comparison to that of the commercial product.18) The thermal expansion coefficient of the glaze was set at 9.3 × 10−6/°C(50 ~ 500°C), similar to that of the body.
The Frit glaze is composed only of glass, so plasticity and adhesive strength are lacking; thus, a small amount of inorganic binder was included to compensate for the lacking properties. The inorganic binder was composed of clay such as Kaolin and Bentonite. When an inorganic binder is added, the glass transition temperature (Tg), dilatometeric softening point (Tdsp), and half-sphere temperature (T1/2), observed by high temperature microscope, slightly increase for the glaze. This phenomenon was thought to be due to the increased SiO2 and Al2O3 content from the inorganic binder in the Frit. Table 1 shows the composition and thermal properties of the body and glaze.
The mixture of the Frit and inorganic binder was glazed on a 10 inch dish through spray coating, followed by curing for 3 h at the curing temperature of 1100°C. The curing was carried out in the commercial tunnel kiln at H company. The lead-free Frit glaze for the bone china underwent vitrification in advance to produce a powder unlike that of regular glaze, so the vitrification reaction occurred conveniently through high temperature heat treatment of the Frit and inorganic binder mixture, producing the glaze layer.
In order to investigate the chemical strengthening effect of bone china, the specimens were chemically strengthened in a chemical strengthening reactor at 420, 450, 480, and 510°C for 3, 6, and 12 h each using a 100% KNO3 melt. The specimens for chemical strengthening were prepared by cutting the flat portion at the center of the 10 inch plates into dimensions of 20 × 20 mm2.
The hardness of the bone china glaze was measured using a micro hardness tester (Shimadzu, HMV 2T E, Japan). In order to determine the residual stress within the glaze, the specimens were processed to a thickness of 0.2 mm, followed by mirror surface finishing on both sides. The residual stress was measured using a polarizing microscope (Nikon, Optiphot-POL, Japan) and an automatic strain viewer (HanKook Lab, HKL-HPASM-S200, Korea). The glass transition temperature and coefficient of thermal expansion were measured using a Thermomechanical Analyzer (TA, TMA Q400, U.S.A). After the chemical strengthening, the K+ ion penetration depth and concentration were measured using EDS (Energy Dispersive spectroscopy, Oxford, Aztec, UK).

3. Results and Discussion

Figure 1 shows the chemical strengthening results of the ceramic specimens with the various glaze compositions and chemical strengthening temperatures. The newly proposed glaze for chemical strengthening was found to result in hardness improvements of more than approximately 30% compared to the case of the commercial glaze. In the case of composition X, 12 h chemical strengthening at 480°C come to a maximum value of 8.46 GPa; the hardness of the commercial glaze was 6.3 GPa.
The hardness of the glaze before chemical strengthening was around 6.3 ~ 6.5 GPa, which was similar to that of the commercial product (6.3 GPa). Since Al2O3 is already known to strengthen the glass structure and improve its hardness, 19-22) the increase in the Al2O3 content for the proposed glaze was predicted to result in hardness improvement before strengthening. However, because the Na2O content increased simultaneously, this effect was thought to be diminished.
For the chemical strengthening at 420°C, which temperature is lower than the glass transition temperature, the hardnesses of the new glaze compositions increased according to time (Fig. 1(a) and (b)). This result showed that the stress within the glass continued to increase during the dispersion of potassium ions. Although the commercial product showed a similar tendency, change in the hardness plateaued over time when the chemical strengthening temperature was above 450°C. This result was determined to be due to the chemical strengthening temperature approaching the glass transition temperature of 560°C for the commercial glaze. However, for the new glaze compositions with high glass transition temperatures, it was observed that the hardness steadily increased with time even for the chemical strengthening at 480°C. Except for composition X, after 3 h the chemical strengthening at 510°C showed a decreasing trend rather than an increasing one for the other composition glazes (Fig. 1(d)). It was determined that relaxation phenomenon did not occur because the glass transition temperature of the composition X glaze was relatively higher than those of the two other compositions;20) the transition temperature difference resulted from the difference in the alumina content.
Figure 2 shows the change of depth of layer according to various chemical strengthening temperatures and times. It has been reported that during the fabrication of chemically strengthened glass, the chemical strengthening depth or depth of layer (DOL) mostly increase when the chemical strengthening temperature and time are increased.20,23) In order to investigate this effect, the K+ ion penetration depth within the glass was examined using EDS line scanning; Fig. 3 shows the results for the chemical strengthening case at 450°C. As can be observed in each image, the K+ ion dispersion depth increased with time. It was found that the K+ dispersion depth due to chemical strengthening increased with time. According to Nordberg et al., the rate of K+ dispersion is proportional to t1/2.24) Also, the dispersion depth abides by the general Arrhenius equation, and so the depth increases as the temperature increases.25) Despite this, the occurrence of the stress relaxation phenomenon, in which the hardness decreases as the chemical strengthening temperature increases, was due to the viscous behavior near the transition temperature.20) This phenomenon signifies the existence of an industrially optimal processing time and temperature. Thus, for the glaze proposed in this study, in terms of the appropriate strengthening temperature and time, the optimal processing conditions appear to be 480°C and 3 ~ 6 h.
The hardness variation with respect to the temperature for the fixed chemical strengthening time of 3 h is shown in Fig. 4. Compared to the commercial glaze, the proposed glaze for chemical strengthening was found to improve the hardness by more than 30%. In the case of composition X, a hardness of approximately 8.3 GPa was obtained through chemical strengthening at 510°C for 3 h, while the hardness of the commercial glaze was 6.3 GPa.
The increase in the hardness through chemical strengthening was thought to be due to an increase in the internal stress. Fig. 5 shows polarized microscope images of the newly proposed glaze and commercial glaze specimens after chemical strengthening. As can be observed in the figure, the newly proposed glaze can be observed to have four different colors, representing the glaze layer surface, glaze layer center, reaction boundary layer between the glaze and body, and the body. Fig. 6 shows observation results obtained using an automatic strain viewer for the residual stress of specimen X, which underwent chemical strengthening at 480°C for 12 h. As can be observed, the compressive strength of the surface layer (approximately 162.8 MPa) is clearly shown and the tensile stress of the reaction boundary layer can be observed. For the commercial product that did not undergo chemical strengthening, a stress of 43.3 MPa was obtained using the thermal expansion coefficient difference between the glaze and body, according to Eq. (1),26) shown below.
(1)
σgl=E(T0-T1)(αgl-αb)
Here, σgl: residual stress within the glaze, E : Young’s modulus of the glaze, T0 : temperature with no residual stress within the glaze, T1 : new temperature, αgl : thermal expansion coefficient of the glaze, αb: thermal expansion coefficient of the body
As found in the previous study, compressive stress is generated in bone china glaze due to the reaction boundary layer, which has a high thermal expansion coefficient.16) Currently, the needle-like boundary layer was predicted to be anorthite (CaO·Al2O3·2SiO2), with a very high thermal expansion coefficient of around 15 ~ 16 × 10−6/°C.27) Figs. 7 and 8 show the microstructure and EDS composition analysis results for specimen X. The needlelike phase was also observed through a polarized microscope and was found to have a relatively higher Al2O3 content compared to the glass layer; the needlelike phase did not contain any Zn component. Additionally, calcium phosphate particles were observed. According to the report of Ichiko, this was predicted to be hydroxyl apatite, with a very high thermal expansion coefficient of around 14 × 10−6/°C.
On the other hand, for the commercial product (Fig. 7(a)), the reaction boundary layer was not observed to form. Its cause was predicted to be due to one of the following: 1) the temperature was too low to induce crystallization because the curing temperature of the commercial product was low at about 1100°C or 2) the Al content within the commercial Frit was relatively low. For the newly proposed glaze, the Al2O3 content was high at over 40% and the Ca concentration was relatively low in the glaze compared to the body, dispersing the Ca ion into the glaze and providing an advantage for the formation of a reaction boundary layer between the glaze and body.
The previous study revealed that sufficient curing of the bone china glaze at 1200°C produced a calcium phosphate compound and Anorthite layer with a large thermal expansion coefficient in the middle layer between the glaze and body, increasing the surface compressive stress of the glaze layer during the cooling process. However, the maximum effect obtained through the curing temperature increase resulted in a hardness increase of only about 5%. Another method of ceramic hardness enhancement was to form low thermal expansion crystalline phases in the glaze.28) However, it is difficult to apply to bone china, because its glaze loses glossy.
Therefore, the glaze for chemical strengthening proposed in this study was expected to provide the basis for obtaining a high hardness product while maintaining the transparency of the bone china glaze.

4. Conclusions

In order to improve the surface hardness of high-quality ceramic bone china, a new glaze composition for effective chemical strengthening was proposed.
The proposed glaze doubled the amounts of Na2O and Al2O3 for chemical strengthening. Chemical strengthening of the bone china with the proposed glaze applied resulted in a hardness improvement of more than 30%. The optimal conditions for chemical strengthening of 480°C for 12 h or 510°C for 3 h were expected to be sufficient to reach the highest property values.
Although a chemically strengthened layer of greater than 40 μm was formed through the chemical strengthening process, chemical strengthening with excessive temperature increases or extended time durations resulted in a decreasing hardness trend, and this was in agreement with the case of general chemically strengthened glass. The surface compressive stress obtained through chemical strengthening was more than 160 MPa, which was a hardness increase of more than 3 times the compressive stress due to the thermal expansion between the glaze and body.

Acknowledgments

This work was supported by the Development of Other Technology Program (Grant No.: 10070453) funded By the Ministry of Trade, Industry and Energy (Korea).

Fig. 1
Change of hardness according to chemical treatment temperatures and times.
kcers-2018-55-3-09f1.jpg
Fig. 2
Change of depth of layer according to various chemical strengthening temperatures and times.
kcers-2018-55-3-09f2.jpg
Fig. 3
Depth profile of potassium and sodium according to chemical strengthening times at 450°C.
kcers-2018-55-3-09f3.jpg
Fig. 4
Change of hardness according to chemical strengthening temperatures for 3 h.
kcers-2018-55-3-09f4.jpg
Fig. 5
Polarizing micrographs of glaze layer section (X400): (a) sample X, (b) Y, (c) Z strengthened chemically at 480°C for 12 h and (d) commercial product without treatment.
kcers-2018-55-3-09f5.jpg
Fig. 6
Residual stress in the glaze layer section: (a) sample X strengthened chemically at 480°C for 12 h and (b) commercial product without treatment.
kcers-2018-55-3-09f6.jpg
Fig. 7
Microstructures of glaze layer sections of (a) commercial product without treatment and (b) sample X.
kcers-2018-55-3-09f7.jpg
Fig. 8
EDS results of the X glaze layer sections: (a) glaze, (b) needlelike crystalline phase and (c) calcium phosphate phase.
kcers-2018-55-3-09f8.jpg
Table 1
Compositions of Body and Glaze of Bone China (wt%)
X Y Z Ref +
SiO2 60.5 61.0 59.0
Al2O3 13.0 12 10.0 7.4
B2O3 2.0 2.0 3.0

CaO 2.0 3.0 3.0
MgO 3.0 2.0 3.0 RO 20 ()
ZnO 5.5 5.5 5.5

Na2O 12.0 13 13 6.3
K2O 2.0 1.5 1.5
Li2O - - -- R2O 6.0 ()

etc. 5.0

Therm. Frit / Frit+Binder F F+B F F+B F F+B F F+B
CTE × 10−6/°C (100 - 300°C) 9.7 8.3 9.1 7.3 9.3 8.5 8.2 7.9
Tg(°C)* 592 648 598 615 584 618 481 494
Tdsp(°C)** 627 696 632 653 618 656 535 544
T1/2(°C)*** 1009 1134 1015 1079 989 1061 950 1012

+ Commercial Frit

* Tg : Glass Transition Temperature (1013.3 Poise)29)

** Tdsp : Dilatometric Softening Point (1011.3 Poise)30)

*** T1/2 : Half Sphere Temperature measured by High Temp. Microscope (104.6 Poise)30)

Unable to publish

REFERENCES

1. WRH. Ramsay, K. Sutton, and EG. Ramsay, “Bow Porcelain: Glaze Compositions Associated with the Phosphatic Ware ~ 1742-1774,” Proc R Soc Victoria, 123 [2] 161-71 (2004).

2. SAF. Batista, PF. Messer, and RJ. Hand, “Fracture Toughness of Bone China and Hard Porcelain,” Br Ceram Trans, 100 [6] 256-59 (2001).

3. SR. Braganca, CP. Bergmannm, and H. Hubner, “Effect of Quartz Particle Size on the Strength of Triaxial Porcelain,” J Eur Ceram Soc, 26 [16] 3761-68 (2006).
crossref
4. G. Stathis, A. Ekonomakou, CJ. Stournaras, and C. Ftikos, “Effect of Firing Conditions, Filler Grain Size and Quartz Content on Bending Strength and Physical Properties of Sanitary Ware Porcelain,” J Eur Ceram Soc, 24 [8] 2357-66 (2004).
crossref
5. ADN. Junior, D. Hotza, VC. Soler, and ES. Vilches, “Analysis of The Development of Microscopic Residual Stresses Particles in Porcelain Tile,” J Eur Ceram Soc, 28 [14] 2629-37 (2008).
crossref
6. X. Cheng, S. Ke, Q. Wang, H. Wang, A. Shui, and P. Liu, “Characterization of Transparent Glaze for Single-Crystalline Anorthite Porcelain,” Ceram Int, 38 [6] 4901-8 (2012).
crossref
7. DU. Tulyaganov, S. Agathopoulos, HR. Fernandes, and JMF. Ferreira, “The Influence of Incorporation of ZnO-containing Glazes on the Properties of Hard Porcelains,” J Eur Ceram Soc, 27 [2] 1665-70 (2007).
crossref
8. CB. Ustundag, YK. Tur, and A. Capoglu, “Mechanical Behavior of A Low-Clay Translucent White Ware,” J Eur Ceram Soc, 26 [1-2] 169-77 (2006).
crossref
9. ED. Spinosa, and KJ. Davies, “Lead-Free Glaze or Enamel for Use on Ceramic Bodies,” US Patent, 5,447,891 A. September. 29. 1993.
crossref
10. Y. Tokunaga, “Lead-free Frit Glaze,” US Patent, 5,362,687 A. February. 4. 1992.

11. RO. Knapp, “Low-Temperature Lead-Free Glaze for Alumina Ceramics,” US Patent, 5,677,250. October. 17. 1994.

12. A. Kara, and R. Stevens, “Interactions between an ABS Type Leadless Glaze And a Biscuit Fired Bone China Body During Glost Firing. Part II: Investigation of Interactions,” J Eur Ceram Soc, 22 [7] 1103-12 (2002).

13. V. Rosa, HN. Yoshimura, MM. Pinto, C. Fredericci, and PF. Cesar, “Effect of Ion Exchange on Strength and Slow Crack Growth of a Dental Porcelain,” Dent Mater, 25 [6] 736-43 (2009).
crossref
14. KJ. Anusavice, C. Shen, and RB. Lee, “Strengthening of Feldspathic Porcelain by Ion Exchange and Tempering,” J Dent Res, 71 [5] 1134-38 (1992).
crossref
15. DH. Kim, JH. Maeng, YS. Han, HT. Kim, SC. Choi, and HJ. Kim, “The Mechanical Properties of Porcelain with Thermally and Chemically Induced Residual Stress on Glaze,” J Korean Ceram Soc, 51 [5] 487-91 (2014).
crossref
16. HJ. Kim, DH. Kim, DM. Kim, JH. Choi, YS. Han, SM. Lee, and HT. Kim, “The Generation of the Residual Stress in ABS Type Glaze of Commercial Bone China,” J Eur Ceram Soc, 36 [3] 899-903 (2016).
crossref pdf
17. HJ. Kim, YS. Han, DH. Kim, DM. Kim, JH. Choi, SM. Lee, Y. Kim, and HT. Kim, “Improvement of Glaze Hardness in Commercial Bone China,” J Korean Ceram Soc, 52 [6] 508-13 (2015).
crossref
18. Y. Nagashima, “Strengthening of Glass and its Structure; from Viewpoints of Fracture and Chemical Strengthening Performance (in Japanese),” New Glass, 30 [114] 3-10 (2015).
crossref pdf
19. S. Inaba, and S. Fujino, “Mechanical Properties of Glass (in Japanese),” New Glass, 23 [4] 46-52 (2008).

20. Y. Nagashima, “Chemically Strengthened Glass - from View Point Glass for Mobile Display (in Japanese),” New Glass, 26 [1] 5-10 (2011).

21. MB. Volf, Chemical Approch to Glass; pp. 300-1 Elsevier, Amsterdam, 1984.

22. H. Scholze, Glass; pp. 272-73 Springer-Verlag, New York, 1991.

23. JH. Maeng, “Chemical Strengthening of Soda-Lime Sheet Glass (in Korean),” 40-6 PhD Thesis, Hanyang University, Seoul2014.

24. ME. Nordberg, EL. Mochel, HM. Garfinkel, and JS. Olcott, “Strengthening by Ion Exchange,” J Am Ceram Soc, 47 [5] 215-19 (1964).

25. R. Gy, “Ion Exchange for Glass Strengthening,” Mater Sci Eng, B, 149 [2] 159-65 (2008).
crossref
26. WD. Kingery, “Factors Affecting Thermal Stress Resistance of Ceramic Materials,” J Am Ceram Soc, 38 [1] 3-15 (1955).
crossref
27. M. Tribaudino, RJ. Angel, F. Camara, F. Nestola, D. Pasqual, and I. Margiolaki, “Thermal Expansion of Plagioclase Feldspars,” Contrib Mineral Petrol, 160 [6] 899-908 (2010).
crossref
28. S. Ghosh, KS. Pal, N. Dandapat, J. Ghosh, and S. Datta, “Glass-Ceramic Glaze for Future Generation Floor Tiles,” J Eur Ceram Soc, 33 [5] 935-42 (2013).
crossref
29. M. Ahmed, and DA. Earl, “Characterizing Glaze-Melting Behavior via HSM,” Am Ceram Soc Bull, 81 [3] 47-51 (2002).
crossref
30. J. Partyka, K. Gasek, K. Pasiut, and M. Gajek, “Effect of Addition of BaO on Sintering of Glass-Ceramic Materials from SiO2.-Al2O3-Na2O-K2O-CaO/MgO System,” J Therm Anal Calorim, 125 [3] 1095-103 (2016).

30. Journal of the Korean Ceramic Society, 55 [3] 1-5 (2018).
crossref pdf
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI