물유리의 수분 함량 및 열처리 온도에 따른 다공체의 특성
공양표, 서상훈, 김종호, 서동수
충남대학교 재료공학과
Characteristics of Porous Ceramics Depending on Water Content of the Water Glass and Heat Treatment Temperature
Yang-Pyo Kong, Sang-Hun Seo, Jong-Ho Kim, Dong-Soo Suhr
Department of Material Science and Engineering Chungnam National University
Porous ceramics which have closes pore were fabricated by heat treatment at 100$∼$ 600$^{circ}C$ for 30 min using dried water glasses with 25, 35, and 45 wt$%$ water contents. Size and distribution of the closed pore were varied depending on the water contents and heat treatment temperature. The expansion procedure could be distinguished by two stages. The frist stage occurred around loo$%$ due to the evaporation of water and the second stage occurred at 200$∼$400$^{circ}C$ due to the decomposition of Si-OH compounds. The specimen was not expanded successfully because of the softening of the dried water glass at 500$∼$600$^{circ}C$.
Key words: Water glass, Porous ceramics, Closed pore, Water content, Heat treatment, Expansion
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI