자전연소합성법을 이용한 리튬이차전지용 양극활물질 LiCoO2의 제조 및 특성 |
류명한, 이종현1, 원창환2, Hayk H. Nersisyan3 |
충남대학교 금속공학과 1한국원자력연구 2충남대학교 금속공학 3충남대학교 급속응고신소재연구소 |
Synthesis and Characteristics of LiCoO2 Powders Prepared by SHS Process |
|
|
|
|
|
ABSTRACT |
LiCoO$_2$ as the cathode activity material for lithium secondary battery was prepared from a homogeneously mixed powder of LiNO$_3$/Co by SHS process under argon gas. The characteristics of powder including electrochemical properties were investigated according to various reaction conditions. The reaction temperature/velocity and the size of LiCoO$_2$ were controlled by Li/Co molar ratio and a cooling rate of the specimen, respectively. The maximum discharge capacity was 145 mAh/g on 1.05 Li/Co molar ratio and the relatively stable cycling characteristic with 6.4% of capacity fading was obtained after 10th charging-discharging test. |
Key words:
$LiCoO_2$, SHS process, Discharge capacity |