| 알루미나가 첨가된 Yttria 안정화 Tetragonal Zirconia Polycrystals 소결체의 특성 |
| 양성구, 정재욱1, 강종봉2 |
경남대학교 공동기기센터(대학원 재료공학과)
1경남대학교 대학원 재료공학과
2경남대학교신소재공학부 |
| Characteristics of Sintered Yttria Stabilized Tetragonal Zirconia Polycrystals(3Y-TZP) with Alumina |
|
|
|
|
|
|
|
| ABSTRACT |
|
3Y-TZP containing 0.3∼1.2 wt% of $Al_2$O$_3$ was prepared by slip-casting after attrition milling. The specimen was sintered at 1390∼151$0^{circ}C$ and mechanical characterization and microstructure analysis were conducted. Monoclinic content of the specimen was calculated by XRD. The apparent density of specimen increased with increasing sintering temperature. While above 1470%, the formation of m-ZrO$_2$ degraded the density. The microhardness of specimen decreased with temperature because monoclinic phase increased wit the grain growth. The specimen containing $Al_2$O$_3$ below 0.9 wt% sintered at 143$0^{circ}C$ showed the highest microhardness of 1360 Hv. |
| Key words:
Zirconia, 3Y-TZP, Phase transformation, m-$ZrO_2$ |
|
|
|